KATANA™ Zirconia HTML PLUS
Inside Dental Technology delivers updates on digital workflows, materials, lab techniques, and innovation in dental technology through expert articles and videos.
February 1, 2022
Volume 13, Issue 2, February 2022
Page(s): p. 29
1. Multilayer zirconia allows a unified sintering schedule to be used for the entire line of multilayer materials, including STML and UTML.
2. Unparalleled flexural strength of 1,150 MPa makes it suitable for a variety of cases within minimal thickness.
3. Seamless multilayered technology eliminates visible transition lines and optimizes layer balance for improved natural color.
4. Fast processing and easy handling allow for superior finishing and next-level restorations.
5. Material consistency and fitting accuracy after the final sintering process reduce remanufacturing risk, with no waste of time and materials.
KATANA Zirconia HTML PLUS is characterized by proprietary raw zirconia powder made in Japan that supports high-speed sintering up to 3-unit bridges. Improved physical properties include all light transmittance at 45% versus 43% of the previous version of HTML without compromising flexural strength of 1,150 MPa. This innovative multilayer material will empower your dental laboratory with more efficiency and exceptional quality.
Specifications:
• Minimal Wall Thickness: 0.4 mm for anterior crown and 0.5 mm for posterior crown
• Shades: 14
• Diameter: 98.5 mm
• Thicknesses: 14 mm, 18 mm, 22 mm
• Applications: Monolithic crowns, monolithic bridges, cut-back frameworks, and frameworks